CA80S has good fluidity, long workable time and low water demand, ideal to produce castables of good working ability and excellent mechanical strength property without any additives, also it suits very well to be used in high temperature environment or hot summer time.
| Item/Grade | CA80 | |||
|---|---|---|---|---|
| CA80 | CA80S | |||
| Chemical Composition | ω (SiO2) ≤/% | 0.5 | 0.5 | |
| ω (Al2O3)/% | 78.0-81.0 | 78.0-81.0 | ||
| ω (Fe2O3) ≤/% | 0.2 | 0.2 | ||
| ω (CaO)/% | 17.5-20.5 | 17.5-20.5 | ||
| ω (MgO) ≤/% | 0.4 | 0.4 | ||
| ω (R2O) ≤/% | 0.4 | 0.4 | ||
| ω (S) ≤/% | / | / | ||
| ω (Cl) ≤/% | / | / | ||
| Fineness | d50/μm | 5-8 | 5-8 | |
| -45μm ≤/% | 5.0 | 5.0 | ||
| Setting Time | Initial Setting Time (min) | 30-90 | 90-150 | |
| Final Setting Time (min) | 90-180 | 270-360 | ||
| Strength (ISO) | Flexural Strength/Mpa | 24h | 5.0-7.5 | 5.0-7.5 |
| 72h | 6.0-8.5 | 6.0-8.5 | ||
| Compressive Strength/Mpa | 24h | 30-40 | 30-40 | |
| 72h | 40-50 | 40-50 | ||
| 325M ≤/% | / | / | ||
| Specific Surface Areas ≥/ (㎡/kg) | / | / | ||